Uniform and dry SiO2 beads with the Encapsulator

Encapsulator B-390 / B-395 Pro: Manufacturing of dry spherical monodisperse SiO2 beads with a size of 430 μm
Uniform and dry SiO2 beads with the Encapsulator
Advanced ceramic materials are of high interest due to their specific and favorable properties such as hardness, durability, optical behavior compared to traditional materials. SiO2 among other oxides such as Al2O3, TiO2 and ZrO2, are common raw materials. In the manufacturing process of advanced materials, granulation is one of the important steps. Usually, large and uniform particles are desired.This application note describes the production of spherical and uniform SiO2 beads having an average size of approximately 430 μm in diameter. The Encapsulator B-395 Pro was applied to obtain and the Rotavapor® R-300 to dry the beads. Using the presented technique, the particle size of the final beads can be varied in the range between 300 and 1000 μm.

Registre-se para fazer download

Gostaríamos de enviar para você outras informações relevantes em breve como, por exemplo, notas de aplicação, guias, webinars e convites para seminários, que podem ser do seu interesse. Para isso, gostaríamos de solicitar sua autorização para permanecer em contato. Você pode descobrir mais sobre seus direitos e como utilizamos e processamos seus dados pessoais em nossa Política de Privacidade.

Instrumentos relacionados

Aplicações semelhantes